C27000 Brass Steel Brass Copper-Steel Clad Plate 0.15mm C2700/If/ C2700 H65 Alloy
Product description
Non-ferrous Metal & Products > Copper
BRASS - STEEL - BRASS
Multilayer strips CuZn35 St CuZn35 Technical Requirements (H65/IF/H65,C2700/IF/ C2700)
Production process:
Cold rolling and rolling composite
Description
Multilayer bimetal strip CuZn35-St-CuZn35is made of low-carbon steel strip, clad on both sides with CuZn35.
Composition
| H1 | BRASS CuZn35 | |||
| H | STEEL | |||
| H2 | BRASS CuZn35 |
- Base - low-carbon quality steel, grade IF(Interstitial Free Steel)/SPHC/ DC04, with chemical composition acc. to GBT3524-2015,
- Hot-rolled carbon and low alloy structural steel strips
- Coating - brass CuZn35 with chemical composition acc. to GBT3524-2015,.
The thickness of cladding layers h1 and h2 is the same for both sides and varies from 4 to 6% of the finished strip thickness. Upon customer's request, the thickness of the cladding layer can be up to 10% on each side.
Classification and range
By state of material:
- soft - Annealing ,HV90-110,
- half-hard ,HV 110-140
- hard - T,HV 160-180
By type of edge:
- sheared edge - O
- mill edge - Н
Technical characteristics
| Type | ThicknessH, mm | Thicknesstolerance, mm | Width B, mm | Widthtolerance, mm | Length, mm | Internal coil diameter ØID, mm | Coilweight, kg |
| Strip | 0,10 - 0,80 | from (±0,005) to (±0,03) | 6 - 60 | (±0,1) | off-gage | 80 / 100 / 200 / 300 / 400 | 10 - 100 |
| 60 - 220 | from (±0,1) to (±0,2) | 50 - 500 | |||||
| 0,81 - 4.00 | from (±0,03) to (±0,005) | 20 - 60 | (±0,1) | off-gage | 300 / 400 / 500 | 10 - 100 | |
| 60 - 220 | from (±0,1) to (±0,2) | 50 - 500 | |||||
| Band | 0,50 - 4,00 | from (±0,02) to (±0,005) | 50 - 220 | from (±0,1) to (±0,2) | 1000 - 3000 | - | - |
For strips with mill edge width tolerance is (±1,0) mm.
Production of other sizes according to the agreed tolerance is possible.
Mechanical properties
Application
For manufacturing of electrical engineering and automotive industry products, cable armouring.