Accelerator TBBS(NS)-80 , Light White Granule , Used for soles and other rubber products.

Recommendations and Applications:

TBBS is delayed accelerator of NR , BR , IR , SBR and reclaimed rubber , 

especially suitable for carbon black masterbatch containing strong alkaline , 

with well processing safety at operating temperature , 

excellent anti-scorching ability , fast curing rate and imparts high tensile modulus of vulcanizate. 

In low sulfur vulcanization, 

TBBS can be used either alone or along with dithiocarbamate salts and thiuram , 

imparts good aging resistance and modulus of the vulcanizates. With high efficiency and low toxin , 

it has excellent comprehensive performance, it is an ideal substitute for NOBS, 

and called the standard accelerator. 

Widely used to produce radial tyre. It can be used along with aldehyde amine , guanidine , thiuram , 

and as well as anti-scorching agent PVI , form a good vulcanization system. Mainly used in tires , 

rubber soles , rubber hose , belts , cable manufacturing.

NR: 0.5~1.0 PHR TBBS and along with 2.5~3.5 PHR sulfur 

SBR: 1.0~1.5 PHR TBBS along with 0.2 PHR thiuram and 1.5~2.5 PHR sulfur.

Composition:

Pre-dispersed 80% N-Tertiarybutyl-2-benzothiazole sulfennamide in a 20% elastomeric binder

Active Ingredient:

Chemical name:N-Tertiarybutyl-2-benzothiazole sulfennamide

CAS NO.: 95-31-8

Molecule structure:

Physical Properties:

Appearance	Light white granule
Mooney ML(1+4)50℃	≤50
Specific gravity	Approx.1.3 g/cm3
Weight loss after heating (80℃,2h)	≤1.5%

Note:

The information is correct and up to date to the best of Longhi’s knowledge. 

The information and data is just for reference only, concrete information please see the actual test result.